Three-dimensionally ordered macro-/mesoporous alumina（3DOM Al2O3）-supported cobalt oxide and platinum nanocatalysts（xPt/yCo3O4/3DOM Al2O3,Pt mass fraction（x%）= 0-1.4%,Co3O4 mass fraction（y%） = 0-9.2%） were prepared using poly（methyl methacrylate） templating,incipient wetness impregnation and polyvinyl alcohol-protected reduction.The resulting xPt/yCo3O4/3DOM Al2O3 samples displayed a high-quality 3DOM architecture with macropores（180-200 nm in diameter） and mesopores（4-6 nm in diameter） together with surface areas in the range of 94 to 102m^2/g.Using these techniques,Co3O4 nanoparticles（NPs,18.3 nm） were loaded on the 3DOM Al2O3 surface,after which Pt NPs（2.3-2.5 nm） were uniformly dispersed on theyCo3O4/3DOM Al2O3.The1.3Pt/8.9Co3O4/3DOM Al2O3 exhibited the best performance for toluene oxidation,with a T（90%） value（the temperature required to achieve 90%toluene conversion） of 160 ℃ at a space velocity of20000 mL g^（-1） h^（-1）.It is concluded that the excellent catalytic performance of the 1.3Pt/8.9Co3O4/3DOM Al2O3 is owing to well-dispersed Pt NPs,the high concentration of adsorbed oxygen species,good low-temperature reducibility,and strong interaction between the Pt and Co3O4 NPs,as well as the unique bimodal porous structure of the support.