Semi-solid A356 aluminum alloy slurry was prepared by using serpentine channel pouring process, and the influences of the channel diameters and pouring temperatures on the semi-solid A356 aluminum alloy slurry were investigated. The experimental results show that when the channel diameter is 20 and 25 mm, respectively, and the pouring temperature is 640-680 ℃, the average diameter of primary α（Al） grains in the prepared A356 aluminum alloy slurry is 50-75 and 55-78 μm, respectively, and the average shape factor of primary α（Al） grains is 0.89-0.76 and 0.86-0.72, respectively. With the decline in the pouring temperature, the microstructure of semi-solid A356 aluminum alloy slurry is more desirable and a serpentine channel with smaller diameter is also advantageous to the microstructure imProvement. During the preparation of semi-solid A356 aluminum alloy slurry, a large number of nuclei can be produced by the chilling effect of the serpentine channel, and owing to the combined effect of the chilled nuclei separation and melt self-stirring, primary α（Al） nuclei can be multiplied and spheroidized finally.
An innovative one-step semi-solid processing technique of A356 Al alloy,the serpentine channel pouring rheo-diecasting process （SCRC）,was explored.The mechanical properties and microstructures of the tensile samples made by the SCRC technique were tested in the as-cast and T6 heat treatment conditions.The experimental results show that the as-cast ultimate tensile strength can reach about 250MPa and the elongation is 8.6%？13.2%.The ultimate tensile strength can increase approximately 30% higher than that of the as-cast one but there is some slight sacrifice of the plasticity after T6 heat treatment.Under these experimental conditions,the semi-solid A356 Al alloy slurry with primary α1（Al） grains,which have the shape factor of 0.78？0.89 and the grain diameter of 35？45μm,can be prepared by the serpentine channel pouring process.The primary α2（Al） grains are very fine during the secondary solidification stage.Compared with the conventional HPDC process,the SCRC process can improve the microstructures and mechanical properties of the tensile test samples.The advantages of the SCRC process include easily incorporating with an existing HPDC machine,cancelling the preservation and transportation process of the semi-solid alloy slurry,and a higher cost performance.