The microstructure evolution of a new directionally solidified（DS） Ni-based superalloy used for gas turbine blades after long-term aging at 950 ℃ was investigated.The results show that the γ ＇ phase becomes more regular in dendritic arm and interdendritic area,while both the mass fraction and the size of γ ＇ phase increase gradually with increasing aging time.During long-term aging,the MC carbide dissolves on the edge to provide the carbon for the formation of M23C6 carbide by the precipitation of Cr at the grain boundary.The rose-shaped γ ＇/γ eutectic partly dissolves into γ matrix and the aging promotes it transform into raft-shape γ ＇.The microstructure is generally stable and no needle-like topologically close-packed phase（TCP） can be found after aging for 1 000 h.