Metastable liquid phase separation and rapid solidification in a metastable miscibility gap were investigated on the Cu60Co30Cr10 alloy by using the electromagnetic levitation and splat-quenching.It is found that the alloy generally has a microstructure consisting of a（Co,Cr）-rich phase embedded in a Cu-rich matrix,and the morphology and size of the（Co,Cr）-rich phase vary drastically with cooling rate.During the electromagnetic levitation solidification processing the cooling rate is lower,resulting in an obvious coalescence tendency of the（Co,Cr）-rich spheroids.The（Co,Cr）-rich phase shows dendrites and coarse spheroids at lower cooling rates.In the splat quenched samples the（Co,Cr）-rich phase spheres were refined significantly and no dendrites were observed.This is probably due to the higher cooling rate,undercooling and interface tension.