Methacrylyloxypropyl modified inorganic/organic hybrid mesoporous materials have been synthesized via an HCl catalyzed sol gel process in the presence of citric acid (CA) as a nonsurfactant template, which involves a combination of 3 (trimethoxysilyl)propyl methacrylate (MSMA) and tetraethoxysilane (TEOS) as precursor species.The CA nonsurfactant is removed by extraction with water, resulting in inorganic/organic hybrid mesoporous materials with high surface area (e.g. 900?m 2·g -1 ) and large pore volume (e.g. 0 55?cm 3·g -1 ).The surface area, pore volume and pore diameter increase slightly with increasing the content of CA.The products were characterized by XRD, N 2 adsorption desorption and FT IR.
ABA triblock copolymers containing polyisoprene segments,such as polyisoprene b polystyrene b polyisoprene (PIP b PSt b PIP)and polyisoprene b poly(methyl methacrylate) b polyisoprene(PIP b PMMA b PIP),were prepared with macro iniferter technique.The macro iniferters (PSt CCDCM and PMMA CCDCM)bearing α and ω N,N diethyldithiocarbamyl (DC)groups were synthesized by bulk polymerization of St and MMA with diethyl 2,3 dicyano 2,3 di( p N,N diethyldithiocarbamylmethyl) phenylsuccinate (DDDCS) as a thermal iniferter.The block copolymerization of IP with PSt CCDCM or PMMA CCDCM was carried out under UV light irradiation.The block copolymers were characterized by 1H NMR,GPC and DSC analyses,and the polymerization proceeded as a living polymerization process.