The ductility of TiAl intermetallics can be improved through stabilizing the ductile β phase.New β-stabilized Ti-45Al-xFe-yMo（x,y=1,2,3,4） alloys were designed through adding the β stabilizing elements Fe and Mo.The microstructural evolution and deformation behavior of the Ti-45Al-xFe-yMo alloys were investigated.The results show that the amount of β（B2） phase is increased with the increase of alloying elements.Mo shows a higher capability for stabilizing the β phase than Fe.In the optimized Ti-45Al-3Fe-2Mo alloy,the grains are significantly refined to about 12 μm,and this alloy shows a very good hot ductility at the elevated temperature.
High temperature pre-precipitation （HTPP）took place in7005 alloy at various temperatures after solution treatment and itsinfluence on mechanical properties, corrosion behaviors and microstructure of the alloy was investigated using tensile test, intergranular corrosion （IGC） test, slow strain rate testing （SSRT）, together with microstructural examinations. It is found that Vickers hardness of the aged alloy decreases gradually with decreasing the HTPP temperature, and almost a reverse trend of electrical conductivity is found compared to the hardness changes. Depending on the changes, two HTPP temperaturesof 440 and 420℃ were chosen for comparative study. Results reveal that HTPP alloy tempers exhibit higher resistance to stress corrosion cracking （SCC） and IGC than none pre-precipitate one with an acceptable strength loss due to the substantial enhancement of distribution discontinuity of the coarse grain boundary precipitates （GBPs）, and the coarsening and interspacing effect on GBPs becomes more obvious with decreasing the pre-precipitation temperature.