A novel synthesis method of carbon-coated LiNil/3Mnl/3COl/302 cathode material for lithium-ion battery was reported. The carbon coating was produced from a precursor, glucose, by microwave-pyrolysis method. The prepared powders were characterized by scanning electron microscopy （SEM）, X-ray diffraction （XRD）, X-ray fluorescence （XRF） and charge/discharge tests. XRD results indicate that the carbon coating does not change the phase structure of LiNil/3Mnl/3C01/302 material. SEM results show that the surface of spherical carbon-coated material becomes rough. Electrochemical performance results show that the carbon coating can improve the cycling performance of LiNii/3Mnl/3C01/302. The specific discharge capacity retention of the carbon-coated LiNi1/3Mnt/3Col/30z reached 85.0%-96.0% at the 50th cycle at 0.2C rate, and the specific discharge capacity retention is improved at a high rate.