Polymer nanoemulsion was prepared by high shear emulsion polymerization and its particle diameter was determined. The results showed that the particle diameter reduced with the increase of reaction temperature, initiator concentration, water content and stirring speed. The optimal ratio of constituents of nanopaints each to other was obtained by orthogonal factorization experiments, and the nanopaint with appropiate viscosity and excellent storage stability was prepared when it contains 0.2% of dispersant, 4.7% of alkaline swelling polyacrylate emulsion thickener and 1.4% of nonionic associative polyurethane thickener.
对应口腔环境中 p H值发生明显变化以及形成龋齿的自然现象 ,采用加速试验法研究了新型钛合金在不同 p H值乳酸中浸泡的耐腐蚀性能。研究表明当 p H=4即酸性略高于龋齿发病时酸性条件下 ,新型牙科钛合金能够完全耐乳酸腐蚀。在乳酸中腐蚀形式以点蚀为主 ,且随酸性增强有向晶间腐蚀转变的趋势。ICP分析表明合金在乳酸中的溶解析出物主要是 Fe,Fe的加入不利于合金的耐腐蚀性能。热力学计算表明设计的新型钛合金氧化膜含有 Mn2 O3、Nb2 O5、Zr O2 和 Ti O2 中的全部或部分 ,XPS分析表明氧化膜中的确含有 Mn2 O3、Nb2 O5和 Ti O2 ,主要是 Ti O2 。这三种氧化物致密且 Ti O2 和 Nb2 O5耐腐蚀 ,有利于合金的耐腐蚀性能。