银-二硫化钼复合材料滑动电磨损机理的研究被引量：4: 2009年; 采用粉末冶金方法制备银-二硫化钼复合材料,研究了材料在滑动电磨损状态下的摩擦系数、磨损量和接触电压降变化情况,探讨了电磨损发生过程的机理。研究表明:与纯机械磨损相比,电磨损过程中材料的摩擦系数差别不大;在电磨损过程中发生阳极侵蚀现象,材料从阳极向阴极发生转移,正刷的磨损量大于负刷,纯机械磨损量在二者之间;磨损过程中由于正刷侧的二硫化钼膜厚度大于负刷,以及正刷微观导电点的数量少于负刷,使得正刷的接触电压降高于负刷。; 李庶凤仪杨茜婷王娟陈淑娴王东里孙宇峰; 关键词：磨损量接触电压降

电流密度对CNTs-Ag-MoS2-G复合材料滑动电摩擦磨损性能的影响（英文）: 滑动电接触材料应具有良好的耐磨性能以及出色的导电性能,在航空航天领域中,制造先进的电接触材料尤为重要。实验中采用粉末冶金法制备CNTs-Ag-MoS2-G复合材料,研究了复合材料电摩擦磨损过程中的接触电阻及磨损率的变化,...; 李庶凤仪陈淑娴王娟; 关键词：滑动电接触电弧侵蚀; 文献传递

滑动速度对CNTs-Ag-MoS_2-C_(graphite)复合材料电磨损性能的影响被引量：6: 2009年; 采用粉末冶金方法制备了CNTs-Ag-MoS2-Cgraphite复合材料,研究了滑动速度变化对复合材料在带电状态下摩擦磨损性能的影响。实验结果表明:在电摩擦磨损过程中,随着滑动速度的增大,滑环所黏着的气流厚度增大,使得电刷与滑环接触表面间隙加大,材料表面的接触电阻增大,电压降也随之增大,而摩擦因数呈线性下降趋势;电流作用产生的超温现象,加速了摩擦表面的磨损,带电磨损时的磨损率大于纯机械磨损时的磨损率且随速度增大先降低后提高;材料转移现象及电流化学作用导致正刷的磨损率大于负刷的磨损率。; 李庶凤仪陈淑娴; 关键词：接触电压降磨损率

滑动速度对碳纳米管-银-石墨复合材料电磨损性能的影响: 2010年; 采用粉末冶金法制备了碳纳米管-银-石墨复合材料,研究了圆周速度对复合材料摩擦系数、磨损量的影响。结果表明,当压力一定时,随着速度的加快,机械磨损的摩擦系数减小,而电磨损的摩擦系数增大;复合材料的电磨损量远远大于机械磨损的磨损量,电磨损时磨损量在V=10m/s处出现最小值,而机械磨损的磨损量随速度的加快而减小。; 孙宇峰徐屹凤仪; 关键词：碳纳米管-银-石墨复合材料磨损量

铜-二硫化钼复合材料的显微组织与性能研究被引量：2: 2008年; 采用粉末冶金法在H2保护气氛下制备Cu-MoS2复合材料,对其进行物相分析和显微组织观察。通过测试密度、硬度、抗弯强度及电阻率,研究MoS2含量变化对复合材料组织与性能的影响。结果表明,MoS2含量不同,烧结产物发生变化,对复合材料的组织与性能影响较大。在烧结过程中,MoS2与基体发生反应,生成铜钼硫化合物、Cu的硫化物和金属Mo。复合材料中物相分散均匀,随MoS2含量增加,基体铜相不断减少,化合物增多,金属Mo弥散镶嵌其中;材料的密度不断减小;随MoS2含量增加,硬度先增后减,再回升;抗弯强度总体呈下降趋势;电阻率明显增大。; 陈淑娴凤仪李庶解育娟李京徽王东里; 关键词：显微组织

Influences of MoS2 contents on sintering process and properties of Cu-MoS2 composites被引量：2: 2008年; CHEN Shu-xian FENG Yi LI Shu XIE Yu-juan; 关键词：硫化铜 X射线光电子能谱热力学分析

Ag-MoS2复合材料电磨损表面膜结构和形成机理研究(英文)被引量：8: 2009年; 采用粉末冶金方法制备了Ag-MoS2复合材料。初压压力300MPa,在H2保护气氛下烧结并保温1h,经500MPa压力的复压过程制得复合材料,用XRD对烧结后的材料进行了物相分析。对材料进行电磨损实验,并对磨损后的材料表面进行XPS分析。结果表明,复合材料在烧结过程中Ag基体和MoS2并未发生化学反应,而在磨损过程中,由于电流和化学作用,材料表面产生了MoO3,MoO2,同时由粘着作用从对磨环转移到电刷表面的铜与大气分子发生化学反应产生了Cu2O,CuOandCu2S。表面膜的存在降低了材料的摩擦系数,影响着材料的电磨损性能。; 李庶凤仪杨茜婷陈淑娴王娟; 关键词：电磨损表面膜

Influence of adding carbon nanotubes and graphite to Ag-MoS_2 composites on the electrical sliding wear properties被引量：5: 2010年; Silver matrix composite brushes were fabricated by means of powder metallurgy, which included pressing at 300 MPa and then sintering for 1 h in pure H2 protective atmosphere at 700 ℃ and repressing at 500 MPa. Four kinds composites with different compositions were produced, and the mechanical properties and electrical wear performance were investigated. The results showed that the composite added with carbon nanotubes had a higher hardness and strength, a lower contact voltage drop and an excellent anti-wear property in electrical sliding wear, because of the reinforcement ability of carbon nanotubes. Adding graphite to the composite also decreased the wear loss and contact voltage drop, because graphite had an electrical current conducting ability which not only made the current pass the lubricating films easily but also eliminated and reduced the arc and spark effectively.; Shu LI Yi FENG Xiting YANG; 关键词：GRAPHITE

室温及气氛条件下铜基自润滑复合材料的摩擦磨损性能研究被引量：7: 2009年; 采用粉末冶金法制备了3种铜基自润滑复合材料,分别考察了它们在室温及气氛条件下的摩擦磨损性能,通过对复合材料的力学性能和磨痕表面形貌、成分的分析,探讨其摩擦磨损机制。结果表明:Cu-9%石墨、Cu-4.5%石墨-4.5%MoS2、Cu-9%MoS2复合材料的密度、硬度和抗弯强度值都依次增大;室温条件下,因石墨与Cu的硫化物协同润滑作用,Cu-4.5%石墨-4.5%MoS2复合材料的摩擦磨损性能最好;气氛条件下,因Cu的硫化物发挥了其自润滑作用,Cu-9%MoS2复合材料表现出最佳的减摩耐磨性能,而Cu-4.5%石墨-4.5%MoS2复合材料次之;铜基自润滑材料的基体强度与固体润滑膜的覆盖率,是影响摩擦磨损机制转变的关键因素。; 陈淑娴凤仪李庶解育娟; 关键词：铜基复合材料自润滑磨损率

MoS_2含量对Cu-MoS_2复合材料烧结过程的影响被引量：8: 2009年; 采用粉末冶金法在保护气氛下制备Cu-MoS2复合材料,用X射线衍射(XRD)和光电子能谱分析(XPS)技术对烧结前、后的试样进行物相和成分分析。研究二硫化钼的含量对复合材料烧结过程和性能的影响。通过热力学分析对烧结过程中的反应进行了讨论。结果表明,在烧结过程中MoS2并未与H2反应,而只与基体铜发生两步反应,分别生成复杂的铜钼硫化合物、Cu的硫化物和单质Mo。且随着MoS2含量的增加,烧结产物有规律地发生变化,复合材料的抗弯强度大幅度减小,电阻率明显升高。热力学分析与XRD和XPS测试结果相吻合。; 陈淑娴凤仪李庶解育娟李京徽王东里

渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心　互联网出版许可证　新出网证(渝)字10号

国家自然科学基金(50741003)