In this work,the influence of a small-molecule material,tris(8-hydroxyquinoline) aluminum (Alq 3),on bulk het-erojunction (BHJ) polymer solar cells (PSCs) is investigated in devices based on the blend of poly(2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene) (MEH-PPV) and [6,6]-phenyl-C 61-butyric acid methyl ester (PCBM).By dop-ing Alq 3 into MEH-PPV:PCBM solution,the number of MEH-PPV excitons can be effectively increased due to the energy transfer from Alq 3 to MEH-PPV,which probably induces the increase of photocurrent generated by excitons dissociation.However,the low carrier mobility of Alq 3 is detrimental to the efficient charge transport,thereby blocking the charge collection by the respective electrodes.The balance between photon absorption and charge transport in the active layer plays a key role in the performance of PSCs.For the case of 5 wt.% Alq 3 doping,the device performance is deteriorated rather than improved as compared with that of the undoped device.On the other hand,we adopt Alq 3 as a buffer layer instead of commonly used LiF.All the photovoltaic parameters are improved,yielding an 80% increase in power conversion efficiency (PCE) at the optimum thickness (1 nm) as compared with that of the device without any buffer layer.Even for the 5 wt.% Alq 3 doped device,the PCE has a slight enhancement compared with that of the standard device after modification with 1 nm (or 2 nm) thermally evaporated Alq 3.The performance deterioration of Alq 3-doped devices can be explained by the low solubility of Alq 3,which probably deteriorates the bicontinuous D-A network morphology;while the performance improvement of the devices with Alq 3 as a buffer layer is attributed to the increased light harvesting,as well as blocking the hole leakage from MEH-PPV to the aluminum (Al) electrode due to the lower highest occupied molecular orbital (HOMO) level of Alq 3 compared with that of MEH-PPV.
We reviewed the key advantages and development of the QD-display and other light applications based on their color purity,stability,and solution processisibility.Analysis of quantum dot based LEDs and the main challenges facing in this field,such as QD luminescence quenching,QD charging in thin films,and the external quantum efficiency was presented in detail.The description about how different optical down-conversion and structures enabled researchers to overcome these challenges and to commercialize the products to achieve the desirable CRI and color temperature was presented.The recent developments about how to overcome these difficulties have also been discussed in this article.