研究了粉末316L不锈钢添加活化剂的液相强化烧结。在1200～1350℃采用真空烧结,对含量为2%～8%的Cu3P和Fe Mo B两种烧结助剂进行比较,后者采用两种粒度。结果表明:Fe Mo B细粉强化作用最强;增加烧结助剂含量和提高烧结温度可以提高烧结密度;最佳条件为添加6%的Fe Mo B细粉、室温压制、1250℃烧结,烧结密度接近7.70g/cm3。另外,压缩试验表明添加量大于6%后,添加Fe Mo B的烧结制品的塑性比添加Cu3P的塑性要好。
The lubrication effectiveness of the composite lubricants, 50wt% ethylene bis-stearamide （EBS） wax ＋50wt% graphite and 50wt% EBS wax ＋ 50wt% BN, during the powder metallurgy （P/M） electrostatic die wall lubrication and warm compaction was studied. The results show that the combination of 50wt% EBS wax and 50wt% graphite has excellent lubrication performance, resulting in fairly high green densities, but the mixture of 50wt% EBS wax and 50wt% BN has less beneficial effect. In addition, corresponding die temperatures should be applied when different die wall lubricants are used to achieve the highest green densities.