Aiming at deep desulfurization of gasoline,three amphiphilic catalysts [C18H37N(CH3)3]3+x [PMo12-xVxO40](x=1,2,or 3) were prepared and characterized.The amphiphilic vanadium(V)-substituted polyoxometalates were dissolved in water-immiscible ionic liquid([Bmim]PF6),forming a H2O2-in-[Bmim]PF6 emulsion desulfurization system with 30 m% H2O2 serving as the oxidant.The catalytic oxidation of sulfur-containing model oil has been studied in detail under various reaction conditions using this system.The ionic liquid emulsion system showed high catalytic oxidative activity in the treatment of commodity gasoline.Furthermore,the mechanism of catalytic oxidative desulfurization was also elaborated.
PtSnNa/AlSBA-15 catalysts with different amounts of Sn were prepared for propane dehydrogenation.The catalysts were characterized by XRF,BET,H2 chemisorption,NH3-TPD,H2-TPR,and TPO techniques.Test results indicated that the presence of tin not only modified the acid function and the interfacial character between metal and support,but also reduced the coke deposition effectively.Among these catalysts investigated thereby,the PtSn(0.7%)Na/AlSBA-15 catalyst had the best catalytic performance in terms of propane conversion and stability.With the continuous addition of Sn,more amounts of Sn0 species appeared,which was unfavorable to the reaction.The PtSn(0.7%)Na/AlSBA-15 catalyst was parametrically characterized in order to obtain necessary information to integrate the process operating conditions.A weight hourly space velocity of 3 h-1,a reaction temperature of 610 ℃ and a H2/C3H8 molar ratio of 0.25 were found to be optimum conditions for achieving a higher dehydrogenation activity of the catalyst.
PtSnNaGa/ZSM-5 catalysts with different contents of Ga were prepared and characterized by X-ray diffraction (XRD), nitrogen adsorption, hydrogen chemisorption, ammonia temperature-programmed desorption (NH3-TPD), hydrogen temperature-programmed reduction (H2-TPR), and temperature-programmed oxidation (TPO) techniques. The performances of these catalysts for propane dehydrogenation were investigated. The test results indicated that the addition of Ga not only could improve the catalytic stability and propene selectivity, but also could effectively prevent the catalysts from coking. It was found that the PtSnNaGa(0.5 m%)/ZSM-5 catalyst exhibited the best performance in terms of propene selectivity and propane conversion. The high catalytic performance was most probably attributed to the presence of Ga that could strength- en the interaction between metals and the support to stabilize the catalytic active sites.
The present article compares the propane dehydrogenation performance of alumina binder-added PtSnNa/ AlSBA-15 catalysts prepared via three different procedures in comparison with the performance of a binder-free PtSnNa/AlSBA-15 catalyst. All these catalysts have been investigated by reaction tests and some physico-chemical characterizations such as BET, H2 chemisorption, catalytic grain crushing strength, NH3-TPD and TPO analyses. Test results showed that the addition of alumina binder could enhance the mechanical strength of catalyst evidently. Moreover, the different preparation procedures not only modified the characteristics of both acid and metal functions but also affected the coke deposition on the catalysts. Among these catalysts studied, the catalyst prepared by impregnation followed by the agglomeration of alumina binder had exhibited the highest catalytic activity and stability compared with other catalyst samples undergoing different preparation procedures. The possible reason may be attributed to the highest metallic dispersion and the strong interactions among Pt, Sn and the support.
The effect of cerium addition on the catalytic performance of propane dehydrogenation over PtSnNa/ZSM-5 catalyst has been investigated by reaction tests and some physicochemical characterization such as XRD,BET,TEM,XPS,NH 3-TPD,H 2 chemisorption,TPR and TPO techniques.It has been found that with suitable amount of cerium addition,the platinum dispersion increased,while the carbon deposition tended to be eliminated easily.In these cases,the presence of cerium could not only realize the better distribution of metallic particles on the support,but also strengthen the interactions between Sn species and the support.Additionally,XPS spectra confirmed that more amounts of tin could exist in oxidized form,which was advantageous to the reaction.In our experiments,PtSnNaCe(1.1 wt%)/ZSM-5 catalyst exhibited the best catalytic performance.After running the reaction for 750 h,propane conversion was maintained higher than 30% with the corresponding selectivity to propylene of about 97%.
The porous material ATZ with micro-mesopore hierarchical porosity was prepared by alkali treatment of parent HZSM-5 zeolite and applied for propane dehydrogenation. The zeolite samples were characterized by XRD, N2-physisorption, and NH 3-TPD analysis. The results showed that the alkali treatment can modify the physicochemical properties of HZSM-5 zeolite. In this case, the porous material ATZ showed larger external surface area with less acid sites as compared to the HZSM-5 zeolite. It was found out that the alkali treatment of HZSM-5 zeolite could promote the catalytic performance of PtSn/ATZ catalyst. The possible reason was ascribed to the low acidity of ATZ. Furthermore, the presence of mesopores could reduce the carbon deposits on the metallic surface, which was also favorable for the dehydrogenation reaction.
Huang LiZhou ShijianZhou YumingZhang YiweiXu JunWang Li