Multi-walled carbon nanotubes （MWNTs） were wet-milled in the presence of ammonia and cationic surfactant and then used as reinforcements to prepare Ni-P-MWNTs composite coatings by electroless plating. The tribological performances of the composite coatings under dry condition were investigated in comparison with 45 steel and conventional Ni-P coating, Micrographs show that short MWNTs with uniform length and open tips were obtained through the wet-milling process. The results of wear test reveal that the Ni-P-MWNTs composite coatings posses much better friction reduction and anti-wear performances when compared with 45 steel and Ni-P coating. Within the MWNTs content range of 0.74%-1.97%, the friction coefficient and the volume wear rate of the composite coatings decrease gradually and reach the minimum values of 0.08 and 6.22x10-15 m3/（N.m）, respectively. The excellent tribological performances of the composite coatings can be attributed to the introduction of MWNTs, which play both roles of reinforcements and solid lubricant during the wear process.
The precursor prepared by coordinated co-precipitation was direct reduced by hydrogen to ultra-fine fibrous Fe-Ni alloy powder. The effects of concentrations of reactants, pH value, reaction temperature and additive on the preparation of precursor were systematically investigated. The structures, thermal decomposition processes and morphologies of the precursors were characterized by X-ray diffraction (XRD), thermal gravity-differential thermal analysis (TG-DTA) and scanning electron microscoy (SEM). The results show that using 2% polyvinylpyrrolidone (PVP) (in mass fraction) as additive, a well-dispersed precursor with a uniform morphology can be obtained in a solution with Fe2+ and Ni2+ total concentration (1:1) of 0.8 mol/L, pH value of 6.2 at 60 °C, and a pure and well dispersed fibrous iron-nickel powder can be prepared by direct reduction of this precursor in a mixed atmosphere of nitrogen and hydrogen at the temperature of 420 °C.
According to the principles of simultaneous equilibrium and mass equilibrium, a series of thermodynamic equilibrium equations in Ni（II）-Co（II）-C2O4^2--NH3-NH4^＋-H2O system at ambient temperature were deduced. The diagrams of logarithm ion concentrations versus pH values at different solution compositions were drawn. The results show that Ni^2＋ and Co^2＋ can completely precipitate at pH less than 5.0 and the predefined Ni/Co ratios can be well kept in the precursor. The precursor morphology is granular aggregation. However, rod aggregation precursor is obtained in the pH range of 5.0-8.0, and fibre-shape precursor is got at pH value higher than 8.0. The Ni/Co ratios in the above two precursors are not reproduced as that in the feed due to the formhtion of multi-coordinated Ni（NH3）n^2＋ and Co（NH3）n^2＋ （n=1-6）. Modification of precipitation medium is favorable for the precursors to keep the predefined Ni/Co ratios of the feed in the pH range of 2.0-8.6. Meanwhile, the precursors with fibrous morphology can be obtained.