Fe2O3/active carbon（Fe2O3/AC） nanocomposites were readily fabricated by pyrolyzing Fe3＋ impregnated active carbon in a nitrogen atmosphere. The as-prepared composites were studied by X-ray powder diffraction（XRD）, X-ray photoelectron spectroscopy（XPS） and transmission electron microscopy（TEM）. The capacitive property of the composites was investigated by cyclic voltammetry（CV） and galvanostatic charge-discharge test. Physical characterizations show that the γ-Fe2O3 fine grains dispersed in the AC well, with a mean size of 21.24 nm. Electrochemical tests in 6 mol/L KOH solutions indicate that the as-prepared nanocomposites exhibited improved capacitive properties. The specific capacitance（SC） of Fe2O3/AC nanocomposites was up to 188.4 F/g that was derived from both electrochemical double-layer capacitance and pseudo-capacitance, which was 78% larger than that of pristine AC. A symmetric capacitor with Fe2O3/AC nanocomposites as electrode showed an excellent cycling stability. The SC was only reduced by a factor of 9.2% after 2000 cycles at a current density of 1 A/g.
LUO Pei-wenYU Jian-guoSHI Zhi-qiangHUANG HuaLIU LangZHAO Yong-nanLI Guo-dongZOU Yong-cun