A new metastable β type titanium alloy called TB-13 with the combination of excellent strength and ductility was developed successfully.In order to develop a perspective on this new alloy,the influence of several commonly used heat treatments on the microstructure and properties was studied.In solution-treated and quenched samples,a low-temperature aging at 480°C results in the precipitation of finerαphase.The precipitation of coarserαphase plate at higher aging temperature(560°C)leads to the increase of tensile ductility but reduction of strength.During low-temperature aging at 300°C,quite homogeneous distribution of fine isothermalωphase particles was found.The isothermalωphase provides nucleation sites forαphase during two-step aging process and makesαphase extremely fine and disperse uniformly in β matrix.Thus,TB-13 alloy is strengthened and its mechanical properties are improved.