New oxometallides with the formula Ba5Y8 xMn4O21 1.5x(x = 0,1) are prepared through an atmospherecontrolled solid-state reaction.Two single-phase samples with Ba/Y/Mn atomic ratios 5/8/4(Y8) and 5/7/4(Y7) are obtained.The crystal structures and the physical properties of the compounds are investigated by X-ray powder diffraction,magnetization,conductivity,and dielectricity measurements.The Ba5Y8 xMn4O21 1.5x compound is demonstrated to be a Y-deficient solid solution.The solid solution compound Ba5Y8 xMn4O21 1.5x crystallizes into tetragonal symmetry with the space group I4/m.Detailed structure analysis by Rietveld refinement of the X-ray powder diffraction data reveals that the Y vacancies occur preferentially at the Y(2) site.Thermal magnetization measurements indicate the presence of antiferromagnetic interaction between Mn ions in the compounds,and temperature-dependent resistivity measurements show that insulator-semiconductor transitions occur around 175 K and 170 K for the Y8 and Y7 samples,respectively.Strong frequency dependences of the dielectric constant are observed above ～175 K for the two compounds.
Different magnetodielectric effects were observed in Bi1-xGdxFeO3 ceramics depending on gadolinium content. A positive one was observed in the samples with x ≤0.10 at 295K and 16K, and a negative one in the sample with x = 0.4 at 16 K. Structure analysis by x-ray diffraction (XRD) reveals that the samples crystallize in the R3c structure (ferroelectrics) for x<0.08 and in the Pbnm structure (paraelectrics) for x≥0.3 at room temperature. Temperature-dependent dielectric response and x-ray diffraction confirm the occurrence of a structural transition in the Pbnm phase at low temperature for the samples with x ≤0.4. While the positive magnetodielectric effects can be attributed to a coupling of magnetic and crystallographic structures of the R3c phase, the observed negative magnetodielectric effect in the Pbnm phase can be associated with a low-temperature modification of the Pbnm structure. The observed dualsigned magnetodielectric effects suggest that the Bi1-xGdxFeO3 oxides are a good prototype for understanding the magnetodielectric coupling mechanism in this kind of materials.