The influence of stresses on martensitic transformation in Ni50Mn19Fe6Ga25 melt-spun ribbons was studied. X-ray diffraction examination shows that the ribbon has a pure cubic L21 phase at room temperature and that the ribbom surface exhibits [100] preferentially oriented texture, while the [110] axis is about 45°tilted from the normal of the ribbon. By calculating the d spacing at different angles with the length direction of the ribbon, the tension was observed. It was found that the direction of the stress was along [010] direction of the oriented textured grains. During cooling, there is no obvious structural transition observed in as-spun ribbons. However, when the ribbons were annealed at 900 K for 24 h, the tension along [010] direction disappeared and the structural transition from cubic to tetragonal occurred obviously during cooling. It indicates that it is the tension along [010] direction to suppress the martensitic transformation in the as-spun ribbons.
The martensitic transformation for Co50Ni20Ga30 ribbon synthesized by the melt-spinning technique was studied by means of X-ray diffraction and ac magnetic susceptibility. The Co50Ni20Ga30 ribbon, having bcc phase with calculated lattice parameters of a=0.57431 nm at 313 K. It exhibits a structure transition from parent phase to martensite during cooling. The martensitic phase in Co50Ni20Ga30 ribbon is tetragonal structure with lattice parameters of a=b=0.5422 nm and c=0.6401 nm. (c/a＞1). According to the changing of diffraction intensity for martensite and the change of ac magnetic susceptibility, the process of the martensitic transformation can be divided into three parts during cooling from 283 K to 213 K. When the temperature decreasing sequentially from 193 K to 110 K, the structure of the martensite has a cha nge in which the a-axis decreases and c-axis increases. The morphologies of selfaccommodation were observeds. The parallelogram morphology, the diamond morphology and the fork morphology were found.