Graphite-like amorphous carbon film was fabricated by unbalanced magnetron sputtering technique.Raman spectroscopy,atomic force microscopy(AFM)and tribometer were subsequently used to investigate the microstructure and tribological properties of the resultant film.It is found that the deposited carbon film is dominated by sp 2 sites,and the intensity ratio of the D and G peaks is as high as 4.0,which is one order of magnitude larger than that of diamond-like carbon films with high sp 3 content,indicating a more graphite-like structure.However,the as-deposited carbon film exhibits moderately high hardness(13.7 GPa),low internal stress(0.38 GPa)and superior tribological properties with high load bearing capacity(Hertz contact stress about 3.2 GPa)and low wear rate(2.73×10-10 cm3/N.m)in ambient atmosphere.Although it displays a poor wear resistance in water lubricated condition,a superior wear resistance is achieved in oil lubricated condition.Its inherent physical property,the formation of transfer layer and the friction induced chemical reactions may be commonly responsible for its tribological properties.
Wang YongjunLi HongxuanJi LiZhao FeiLiu XiaohongWu YanxiaZhou HuidiChen Jianmin
By using the molecular dynamic simulation method with a fourth-order Runge--Kutta algorithm, a two-dimensional dc- and ac-driven Frenkel--Kontorova （FK） model with a square symmetry substrate potential for a square lattice layer has been investigated in this paper. For this system, the effects of many different parameters on the average velocity and the static friction force have been studied. It is found that not only the amplitude and frequency of ac-driven force, but also the direction of the external driving force and the misfit angle between two layers have some strong influences on the static friction force. It can be concluded that the superlubricity phenomenon appears easily with a larger ac amplitude and lower ac frequency for some special direction of the external force and misfit angle.
Amorphous carbon films with high sp2 concentrations are deposited by unbalanced magnetron sputtering with a narrow range of substrate bias voltage. Field emission scanning electron microscopes （FESEMs）, high resolution transmission electron microscopes （HRTEMs）, atomic force microscopes （AFMs）, the Raman spectrometers, nano- indentation, and tribometers are subsequently used to characterize the microstructures and the properties of the resulting films. It is found that the present films are dominated by the sp2 sites. However, the films demonstrate a moderate hardness together with a low internal stress. The high hardness of the deposited film originates from the crosslinking of the sp2 clusters by the sp3 sites. The presence of the graphite-like clusters in the film structure may be responsible for the low internal stress. What is more important is that the resulting films show excellent tribological properties with high load capacity and excellent wear resistance in humid atmospheres. The relationship between the microstructure determined by the deposition condition and the film characteristic is discussed in detail.
Wang Yong-JunLi Hong-XuanJi LiLiu Xiao-HongWu Yan-XiaZhou Hui-DiChen Jian-Min