Siliconated polyurethane (Si-PU) was synthesized using isophorone diisocyanate (IPDI), hydroxybutyl-terminated polydimethylsiloxane (PDMS), polytetramethylene ether glycol (PTMG), polypropylene glycol (PPG), 1,6-hexanediol (HDO), dimethylol propionic acid (DMPA) and triethylamine (TEA). Based on butyl acrylate (BA), 2, 2, 2-trifluoroethylmethacrylate (TFEMA) and Si-PU as a seed emulsion, a novel core-shell type acrylic-polyurethane hybrid emulsion, containing siloxane and fluorine (F-Si-PU), was prepared by seeded emulsion polymerization. The contents of siloxane and fluorine were determined according to the feed ratio. Fourier transform infrared spectroscopy (FTIR) was used to identify the chain structures of Si-PU and F-Si-PU. Investigation of transmission electron microscopy (TEM) confirmed the core-shell structure of F-Si-PU emulsion. Measurement results of water contact angle and the swelling ratio in water and n-octane for cured film showed that the water and the oil resistances for F-Si-PU had been significantly improved at a suitable content of fluorine and siloxane.
Jing CHAO Xing Yuan ZHANG Jia Bing DAI Zhen GE Lin Lin FENG
A well-defined modification of polytetramethylene glycol (PTMG) was realized by radical grafting with hexafluoropropylene (HFP). The structure of grafted product was confirmed by means of IR, 1H NMR and 13C NMR. The effects of the amount of initiator, reaction time and temperature on the grafting HFP onto PTMG were investigated.
A novel and facile method toward a series of yellow water-borne polyurethane was developed by using an intrinsically colored diol in this paper.The yellow aqueous dispersion PCLD-HENA-PU was synthesized based on isophorone diisocyanate(IPDI), polycaprolactonediol(PCLD) and 2,2-dimethylol propionic acid(DMPA) using a yellow diol N,N-bis(2-hydroxyethyl)-4-nitroaniline (HENA) as a chain extender.Due to the complete reaction of OH group in colorant HENA with NCO group in diisocyanate,a series of stable yello...