A new process of extrusion forming was used to replace the traditional drilling technics.This kind of forming method may improve the structure of materials and anti-deforming capacity,enhancing the life of parts.It is shown by numerical simulations on the forming process of spherical extrusion on bolt-hole.Effects of technological parameters were discussed on spherical surface of extrusion and the diameter of pre-punching hole was determined.It is revealed that the smaller diameter of pre-punching hole,the larger deforming measurement of hole after extrusion.The extrusion stress determines the development trend of pre-punch hole becomes bigger or smaller and the pre-punching hole diameter is the key to control the size of deforming measurement of hole after extrusion.
Both experimental and mechanical analyses were carded out to investigate the characteristics of thickness distribution for tailor-welded tube （TWT） hydroforming with dissimilar thickness. Then, the effects of weld-seam position and thickness difference were also revealed. A multiple-diameter tube was formed to reveal the characteristics and the regularity of thickness distribution during TWT hydroforming. It is indicated that there are obvious fluctuations in thickness distribution though the TWTs have the same expansion ratio. The thinning ratio of thinner tube is bigger than that of thicker tube especially in the zone closed to the weld-seam. The difference in thinning ratio between two tube segments can reach 9%. Consequently, sudden and large fluctuation of thickness appears in the zone nearby the weld-seam. The difference in thinning ratio between thinner and thicker tubes enlarges as the thickness difference increases, but improves as length ratio increases. Different strain states are the main reason to induce nonuniform thickness distribution. The difference in thickness is the main reason to induce different strain states on thinner and thicker tubes.
To reveal the reason of weld-line movement in hydroforming of a tailor-welded tube (TWT) with dissimilar thickness,the stress ratio of axial stress to circumferential stress is derived by mechanical analysis and analyzed between the thicker and thinner tubes,as well as the property of the axial strain. During TWT hydroforming,tensile strain along axial direction happens on the thinner tube. On the contrary,compressive strain happens on the thicker tube. Experiments are conducted to varify the weld-line movement regularity and strain distribution. It indicates that the weld-line moves from the thinner part to the thicker during TWT hydroforming. The thinning ratio of the thinner tube is bigger than that of the thicker tube,especially in the zone near weldline. Stress ratio difference between the thicker tube and the thinner tube is the main reason of weld-line movement and non-uniform thinning ratio distribution.