Near-normal incident infrared reflectivity spectra of （100） MgAl2O4 spinel single crystal have been measured at different temperatures in the frequency region between 50 and 6000 cm^-1. Eight infrared-active phonon modes are identified, which are fitted with the factorized form of the dielectric function. The dielectric property and optical conductivity of the MgAl2O4 crystal are analysed. From TO/LO splitting, the effective Szigeti charges and Born effective charges at different temperatures are calculated for studying the ionicity and the effect of polarization. Based on the relationship between the （LO-TO）1 splitting, which represents the transverse and longitudinal frequencies splitting of the highest energy phonon band in the reflectivity spectrum, and the ionic-covalent parameter, the four main phonon modes are assigned. MgA1204 can be considered as a pure ionic crystal and its optical characters do not change with decreasing temperature, so it may be used as a suitable substrate for high-Tc superconducting thin films.
This paper reports that polarized far-infrared reflectivity measurements have been done on LiGaO2 single crystal along two crystalline taxes at different temperatures. The temperature dependent frequencies of the longitudinal and transverse optical phonon have been obtained from the real part of optical conductivity and the loss function respectively. A small Drude component is observed at frequency below 300 cm^-1 which could arise from Li ions or oxygen deficiencies. The ionicity of LiGaO2 has been studied from the analysis of the Born effective charge of different ions.