Fluoro-terminated hyperbranched(poly(aryl) ether ketone)(HPOP-PEEK-F) with 4-phenoxyphenyl side groups was prepared from A2(2-(4-phenoxyphenyl)-1,4-diphenol) and B3(1,3,5-tris[4-(4-flourobenzoyl) phenoxy]benzene) with a function group ratio of 0.48:1(A2:B3).The chemical structure of HPOP-PEEK-F was confirmed by FTIR and()1H-NMR.The degree of branching(DB) of HPOP-PEEK-F was 0.66 determined by()1H-NMR measurements.The phenyl ethynyl-terminated hyperbranched poly(ether ether ketone)(HPOP-PEEK-PEP) was prepared by the end-capping approach.The HPOP-PEEK-PEP showed high glass transition temperature than HPOP-PEEK-F,but exhibited lower thermal stability.After cross-linking,the glass transition temperature,thermal stability and anti-chemical corrodibility of HPOP-PEEK-PEP were all improved.
Two novel poly(aryl ether ketone)s based on (3 methyl)phenylhydroquinone were synthesized via aromatic nucleophilic substitution reaction. The high molecular polymers were easily obtained because of the high reaction activity of bisphenol monomer. The traces of DSC showed that the T gs of m TPEEK and m TPEEKK were 421 and 432 K, respectively. The two polymers exhibit a high thermal stability and good solubility. The transparent and flexible films were readily prepared with chloroform solution. The film of m TPEEK had a low dielectric constant( ε =2 7).