A series of Pt–V/Ce–Zr–O diesel oxidation catalysts was prepared using the impregnation method. The catalytic activity and sulfur resistance of Pt–V/Ce–Zr–O were investigated in the presence of simulated diesel exhaust. The effect of vanadium on the structure and redox properties of the catalysts was also investigated using the Brunauer–Emmett–Teller method,X-ray diffraction, H2temperature-programmed reduction, CO temperature-programmed desorption, X-ray photoelectron spectroscopy, and Energy Dispersive Spectroscopy. Results showed that the Pt particles were well dispersed on the Ce–Zr–O carrier through the vanadium isolation effect, which significantly improved the oxidation activity toward CO and hydrocarbons. An electron-withdrawing phenomenon occurred from V to Pt, resulting in an increase in the metallic nature of platinum, which was beneficial to hydrocarbon molecular activation.
A monolithic series of Cu-Mn-Ce oxides supported on cordierites with different Cu/Mn/Ce molar ratios were prepared by the in-situ sol-gel method without any binder. The catalysts were characterized by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), X-ray diffraction (XRD), and Brunauer-Emmett-Teller method (BET) and examined in the catalytic combustion of volatile organic compounds (VOCs). The results showed that the well-dispersed nanometer particles of mixed oxides adhered firmly to the cordierite surface. Cu0.15Mn0.3Ce55/cordierite was identified as the most active catalyst. Compared with commercial Pd/Al2O3, Cu0.15Mn0.3Ce55/cordierite showed higher activities for the combustion of various types of VOCs, especially for oxy-derivative compounds which could be lighted off below 200 ℃.