In this study rectangular AlGaN/AlN/GaN heterostructure field-effect transistors(HFETs) with 22-nm and 12-nm AlGaN barrier layers are fabricated, respectively. Using the measured capacitance–voltage and current–voltage characteristics of the prepared devices with different Schottky areas, it is found that after processing the device, the polarization Coulomb field(PCF) scattering is induced and has an important influence on the two-dimensional electron gas electron mobility.Moreover, the influence of PCF scattering on the electron mobility is enhanced by reducing the AlGaN barrier thickness.This leads to the quite different variation of the electron mobility with gate bias when compared with the AlGaN barrier thickness. This mainly happens because the thinner AlGaN barrier layer suffers from a much stronger electrical field when applying a gate bias, which gives rise to a stronger converse piezoelectric effect.
Ni/Au Schottky contacts on AlN/GaN and AlGaN/GaN heterostructures are fabricated. Based on the measured current-voltage and capacitance-voltage curves, the polarization sheet charge density and relative permittivity are analyzed and calculated by self-consistently solving Schrodinger＇s and Poisson＇s equations. It is found that the values of relative permittivity and polarization sheet charge density of AlN/GaN diode are both much smaller than the ones of AlGaN/GaN diode, and also much lower than the theoretical values. Moreover, by fitting the measured forward 1-V curves, the extracted dislocations existing in the barrier layer of the AlN/GaN diode are found to be much more than those of the AlGaN/GaN diode. As a result, the conclusion can be made that compared with AlGaN/GaN diode the Schottky metal has an enhanced influence on the strain of the extremely thinner AlN barrier layer, which is attributed to the more dislocations.
Electron mobility scattering mechanism in AlN/GaN heterostuctures is investigated by temperature-dependent Hall measurement, and it is found that longitudinal optical phonon scattering dominates electron mobility near room temperature while the interface roughness scattering becomes the dominant carrier scattering mechanism at low temperatures （~ 100 K）. Based on measured current-voltage characteristics of prepared rectangular AlN/GaN heterostructure field-effect transistor under different temperatures, the temperature-dependent variation of electron mobility under different gate biases is inves- tigated. The polarization Coulomb field （PCF） scattering is found to become an important carrier scattering mechanism after device processing under different temperatures. Moreover, it is found that the PCF scattering is not generated from the thermal stresses, but from the piezoelectric contribution induced by the electrical field in the thin A1N barrier layer. This is attributed to the large lattice mismatch between the extreme thinner AlN barrier layer and GaN, giving rise to a stronger converse piezoelectric effect.