Light-emitting and photovoltaic properties of copolymers(PFO-FBT) based on 9,9-dioctylfluorene and 4,7-difuran-2,1,3-benzothiadiazole(FBT) units were investigated.The copolymers show two absorbance peaks at around 382 nm and 530 nm,respectively.The relative absorbance at around 530 nm of the PFO-FBT copolymers increases with the increasing FBT content.The EL emissions are red-shifted from 611 nm to 702 nm by increasing the FBT content in the copolymer.The highest EL external quantum efficiency achieved with the device configuration of ITO/PEDOT/PVK/PFO-FBT0.1/Ba/Al is 2.32% with the luminance of 441.3 cd/m2 at a current density of 33 mA/cm2.Efficient energy transfer due to exciton trapping on low band-gap FBT sites was observed.The bulk-heterojunction photovoltaic cell used PFO-FBT50 copolymer as the electron donor and methanofullerene [6,6]-phenyl C61-butyric acid methyl ester(PCBM) as the electron acceptor shows an energy conversion efficiency of 1.13% with open-circuit voltage(Voc) of 0.85 V and short-circuit current density(Jsc) of 3.39 mA/cm2 under AM 1.5 solar simulator(100 mW/cm2),and the edge of the spectral photoresponse is at ～750 nm.
A series of conjugated copolymers derived from 9-ethylhexyl-2,7-carbazole(Cz)and 4,7-di(4-hexylthien-2-yl)- 2,1,3-benzothiadiazole(DHTBT)was synthesized by Suzuki polycondensation.The photo-and electro-luminescent properties of these polymers were investigated.Efficient energy transfer from the Cz segment to the DHTBT unit occurs even if the DHTBT content as low as 1 mol%.PL emission was red-shifted significantly from 645 nm to 700 nm with the increase in DHTBT content by 1-50 mol%.PL efficiencies decrea...
＜正＞Solar cells based on organic molecules or conjugated polymers attract great attention due to their unique a...
Jie Zhang,Wanzhu Cai,Ming Wang,Chunhui Duan,Yong Cao~* (Institute of Polymer Optoelectronic Materials and Devices,Key Laboratory of Specially Functional Materials of Ministry of Education,South China University of Technology,Guangzhou 510640)