Calcined kaolin/TiO2 composite particle material （CK/TCPM） was prepared with TiO2 coating on the surfaces of calcined kaolin particles by the mechano-chemical method. X-ray diffraction （XRD） and scanning electron microscope （SEM） were used to investigate the microstructures and morphologies, respectively. The mechanism of the mechano-chemical reaction between calcined kaolin and TiO2 was studied by infrared spectra （IR）. The results show that TiO2 coats evenly on the surfaces of calcined kaolin particles by Si-O-Ti and Al-O-Ti bonds on their interfaces. The hiding power and whiteness of CK/TCPM are 17.12 g/m^2 and 95.7%, respectively, presenting its similarity to TiO2 in pigment properties.
Barite/TiO2 composite particle (B/TCP) was prepared by coating TiO2 on the surfaces of barite particles through mechano-chemical method. The preparation parameters and pigment properties of B/TCP as well as the interaction mechanism between barite and TiO2 were studied. The results indicated that the mechanical co-grinding process and the proportion of TiO2 affected the properties of B/TCP significantly. B/TCP prepared under optimal conditions was similar to TiO2 in pigment properties. It was mainly the strong electrostatic attraction between barite and TiO2 in water that combined them firmly and then formed B/TCP.
Wang Baikun, Ding Hao, Wang Yongkui, Liang Ning China University of Geosciences (Beijing), Beijing 100083, China