The effects of magnetic field annealing on the properties of Fe48Co52 alloy nanowire arrays with various interwire distances （Di=30-60 nm） and wire diameters （Dw=22-46 nm） were investigated in detail. It was found that the array＇s best annealing temperature and crys- talline structure did not show any apparent dependence on the treatment of applying a 3 kOe magnetic field along the wire during the annealing process. For arrays with small Dw or with large Di, the treatment of magnetic field annealing also had no obvious influence on their magnetic performances. However, such a magnetic field annealing constrained the shift of the easy magnetization direction and improved the coercivity and the squareness obviously for arrays with large Dw or with small Di. The difference in the intensity of the effective anisotropic field within the arrays was believed to be responsible for this different variation of the array＇s magnetic properties after magnetic field annealing.
Hai-lin SuShao-long TangRui-long WangYi-qing ChenChong JiaYou-wei Du