The grain growth behavior in reactive spray formed 7075+2.91 vol percent TiCAl alloy was studied and compared with that of spray formed 7075 Al alloy at semi-solid state. Theeffects of in-situ TiC particles on the microstructure of spray formed 7075 Al alloy were alsoinvestigated. The specimens were heat-treated isothermally at various temperatures between thesolidus and liquidus of 7075 Al alloy for times in the range of 10-60 min, then quenched in water.The microstructure of reheated specimens was characterized using scanning electron microscopy andoptical microscopy. The grain size was measured using a mean linear intercept method. Results showthat the in-situ TiC particles can effectively retard grain growth and refine the grain at a limitedsize. The grain growth exponent in Arrhenius equation increases from 2 to 3, which indicates thatthe in-situ TiC particles have the significant pinning effect on grain coarsening in the semi-solidstate.