A series of Ce-Fe-Zr-O(x)/MgO(x denotes the mass fraction of Ce-Fe-Zr-O,x=10%,15%,20%,25%,30%) complex oxide oxygen carriers for selective oxidation of methane to synthesis gas were prepared by the co-precipitation method.The catalysts were characterized by means of X-ray diffraction and H2-TPR.The XRD measurements showed that MgFeO4 particles were formed and Fe2O3 particles well dispersed on the oxygen carriers.The reactions between methane diluted by argon(10% CH4) and oxygen carriers were investigated.Suitable content of CeO2/Fe2O3/ZrO2 mixed oxides could promote the reaction between methane and oxygen carriers.There are mainly two kinds of oxygen of carriers:surface lattice oxygen which had higher activity but lower selectivity,and bulk lattice oxygen which had lower activity but higher selectivity.Among all the catalysts,Ce-Fe-Zr-O(20%)/MgO exhibited the best catalytic performance.The conversion of the methane was above 56%,and the selectivity of the H2 and CO were both above 93%,the ratio of H2/CO was stable and approached to 2 for a long time.
The Ce-Fe-O mixed oxide with a ratio of Ce/Fe=7:3, which was prepared by coprecipitation method and employed as oxygen carrier, for direct partial oxidation of methane to syngas in the absence of gaseous oxygen was explored. The mixed oxide was characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), and the catalytic performances were studied in a fixed-bed quartz reactor and a thermogravimetric reactor, respectively. Approximately 99.4% H2 se...
A citric acid complex method was employed to prepare Ce/Ni mixed oxides with various Ce/Ni ratios useful for selective oxidation methane to syngas in the absence of gaseous oxygen,and the catalytic activity measurement was investigated in a fixed bed reactor at 800 oC.The prepared oxygen carriers were characterized by various characterization techniques such as TG-DSC,XRD and TPR.The results of TG-DSC indicated that the Ce1-xNixO2 precursor generated a stable phase after the heat-treatment at temperatures above 800 oC.The XRD characterization suggested that some Ce-Ni solid solution was formed when Ni2+ ions was incorporated into the lattice of CeO2,and it led to the generation of O-vacancy which could improve the oxygen mobility in the lattice of oxygen carriers.It was found that Ce0.8Ni0.2O2 gave the highest activity in the selective oxidation methane to syngas reaction,and the average methane conversion,CO and H2 selectivity reached to 82.31%,82.41% and 87.64%,respectively.The reason could be not only attributed to the fitting amount of NiO dispersed on the CeO2 surface and bulk but also to actual lattice oxygen amount increased in oxygen carrier.
The reaction of zinc oxide with methane in the absence and presence of CO2 were theoretically and experimentally investigated using HSC Chemistry 5.1 software and a fixed bed reactor, respectively. In the absence of CO2 at 1193 K, the reduction of ZnO was accompanied with methane cracking, and metallic zinc, CO, and H2 were the main reaction products. This system could be utilized for the co-production of metallic zinc and synthesis gas, in which ZnO was a donor of oxygen. In the presence of CO2, ZnO plays as a catalyst in the CO2 reforming of methane and produces syngas with the average H2/CO ratio of 0.88 at 1193 K, which was close to the total reaction theoretic value of 1. It was also found that higher temperature favored high CH4 and CO2 conversions. XRD technique was used to characterize the ZnO species. The result showed that there were no differences in the peak profiles of the XRD patterns of the ZnO powder obtained before and after passing the CH4/CO2 mixed gases for 6 h at 1193 K. It is suggested that ZnO functions as a catalyst according to the redox cycle and metallic zinc plays the role of intermediate product in this process.
Two-step steam reforming of methane (SRM) is a novel chemical looping process towards the production of pure hydrogen and syngas (synthesis gas), consisting of a syngas production step and a water-splitting step. Renewable energy can be used to drive this process for hydrogen production, especially solar energy. CeO2-Fe2O3 complex oxide oxygen carrier was prepared by the impregnation method and characterized by means of X-ray diffractometer (XRD), Raman spectroscopy (Raman) and hydrogen programmed reduction (H2-TPR). CH4 temperature programmed and isothermal reactions were adopted to test syngas production reactivity, and water splitting reaction was employed to investigate water-splitting activity. Moreover, two-step SRM performance was evaluated by a successive redox cycle. The results showed that CO-uncontaminated H2 and highly selective syngas (with H2/CO ratio close to 2) could be respectively obtained from two steps, and CeFeO3 formation was found in the first redox cycle and proved to be enhanced by the redox treatment. After 10 successive cycles, obvious CeFeO3 phase was detected, which may be responsible for favorable successive redox cycle performances.