The corrosion process of the X70 pipeline steel in 3.0wt% NaCl solution were studied using polarization method, and the chronological characteristics during the entire polarization plot were investigated in detail using EIS technique. In the active region of X70 steel, such as 20mV potential bias applied on open circuit potential (OCP), the impedance spectra was comprised of three parts: a high-frequency capacitive loop, a middle-frequency capacitive loop and a low-frequency inductive component. When positive polarization potential increased, the capacitive loops at high and middle frequency range merged, and the inductive component at low frequency shrunk. At high positive polarization potential bias (500-800mV vs. OCP), the high-frequency capacitive loop and the low-frequency inductive loop exhibited as disheveled points due to the synergism of the inhomogeneity of the corroding material and the localized corrosion. The results were fitted utilizing the equivalent circuits to simulate the impedance spectra and to interpret the electrochemical features shown during the experiments.
The electrochemical features of commercial airfrarne material, Al alloy LY12, in 0.349mol/L neutral sodium chloride (NaCl) and sodium sulfate (NazSO^) solutions were investigated by electrochemical impedance spectroscopy (EIS) and potentiody-namic polarization techniques. The microstructure of the as-tested samples was studied by scanning electron microscopy. The results show that the Nyquist plots of LY12 at different immersion time displayed different features, indicating that the Cl- ions elevate the corrosion rate and inhibit the repassivation of a metastable pit. It also shows that the corrosion product of LY12 formed in SO42- solution isn't easy to dissolve, and it will cover the surface of working electrode in the electrolyte. SEM images indicate that the corrosion apparent area and pit number of LY12 in NaCl solution are greater than that in Na2SO4 solution.