As a means of surface modification process, metal surface nanocrystallization （MSN） has attracted widespread attention and enjoyed a great prospect. However, currently little research is carried out regarding MSN of welded joint. The processes of high energy shot peening （HESP） technology and ultrasonic impact treatment （UIT） were carried out to achieve joint surface nanocrystallization. The grain size of before and after the welded joint surface nanocrystallization were comparatively analyzed with X-ray diffractometer, the surface deformation layer thickness of before and after the welded joint surface nanocrystallization were comparatively analyzed with optical microscopy, the surface hardness of before and after the welded joint surface nanocrystallization were comparatively analyzed with micro hardness machine. The results show that both of the processes can achieve welded joint surface nanocrystaUization and the weld after HESP have smaller grain size, larger deformation layer thickness and higher hardness values than those after UIT. However, HESP is restrained by the shapes and sizes of welding materials, so the UIT process is preferred to use in the general engineering practical applications.