We presented a field electron emission measurement of single crystalline CeB6 nanowires.The nanowires exhibited a low turn-on electric field(7.6 V/μm at 10 μA/cm2),and the deviation of Fowler-Nordheim(F-N) plots from straight line was observed in field electron emission measurements.The field enhancement factors were obtained by separate straight line fitting.The nonlinearity in the F-N plots may be attributed to the non-uniform field electron emission of CeB6 nanowires.The field emission properties of the ...
A facile catalysis-free method was utilized to synthesize functional neodymium hexaboride （NdB6 ） nanowires of single crystal using Nd powders and BCl 3 as starting materials. The XRD pattern confirmed that a single phase NdB 6 could be obtained. Raman-spectra elucidated the active vibrational modes of the hexaborides. The TEM images clearly showed that the hexaborides were submicron in size with a cubic morphology. The field emission of these one-dimensional NdB6 nanowires showed a low field emission turn-on （5.55 V/μm at a current density of 10 μA/cm2 ）, and high current density with a field enhancement factor of 1037. The emission current density and the electric field followed the Fowler-Nordheim （F-N） relationship. The good performance for field emission was attributed to the single-crystalline structure and the nanowire geometry.