The laser bonding technology between the Zr41 Ti14 Cu12 Ni10 Be23 bulk metallic glass and zirconium metal was investigated under welding parameters of 1.3 kW and 7 m/min. The welded bead, microstructure, and micro-hardness of the welded joint were examined by Keyence, transmission electron microscopy, scanning electron microscopy, and Vickers hardness, respectively. The experimental results showed that the Zr41 Ti14 Cu12 Ni10 Be2 bulk metallic glass and zirconium metal were successfully bonded together. The Zr41 Ti14 Cu12 Ni10 Be2 in the base material zone maintained amorphous structure, and the welding fusion zone kept the hardness as high as as-received BMG. Therefore, the laser welding technology can be used to achieve successful bonding of bulk metallic glasses and crystallization metal.
We investigated the effects of heating rate on the process parameters of superplastic forming for Zr55Cu30Al10Ni5 by differential scanning calorimetry. The continuous heating and isothermal annealing analyses suggested that the temperatures of glass transition and onset crystallization are heating rate-dependent in the supercooled liquid region. Then, the time-temperature-transformation diagram under different heating rates indicates that increasing the heating rate can lead to an increase of the incubation time at the same anneal temperature in the supercooled liquid region. Based on the Arrhenius relationship, we discovered that the incubation time increases by 1.08-1.11 times with double increase of the heating rate at the same anneal temperature, and then verified it by the data of literatures and the experimental results. The obtained curve of the max available incubation time reveals that the incubation time at a certain anneal temperature in the supercooled liquid region is not infinite, and will increase with increasing heating rate until this temperature shifts out of the supercooled liquid region because of exceeding critical heating rate. It is concluded that heating rate must be an important processing parameter of superplastic forming for Zr55Cu30Al10Ni5.
We investigated the deformation behaviors of Zr65Cu17.5Ni10Al7.5 in superplastic forming in silicon mould via numerical modeling and experiments. The data needed for the constitutive formulation were obtained from compressive tests to establish a material library for finite-element simulation using a DEFORM 3D software. A constant speed forming process of a micro gear was modeled where the loading force, feature size and amount of deformation in the micro gear in silicon mould were analyzed in detail for the optimal requirements of micro gear forming and the protection of silicon mould. Guided by the modeling parameters, an amorphous metal micro gear was successfully obtained by our home-made superplastic forming system with the optimized parameters(temperature of 683 K, top speed of 0.003 mm/s until the load force reaching limiting value at 1960 N, and a gradually decelerating process for holding the force to the end). Our work gives a good example for optimization of superplastic forming and fabrication of BMGs in microparts.