The effects of weight-average molecular(Mw), molecular weight distribution(MWD), and isotacticity on the linear viscoelastic behavior of polybutene-1 melts are studied. It is observed that the linear viscoelastic region becomes slightly narrower with increasing frequency. In frequency sweeps, the transition of the polymer melts flow from Newtonian flow to power-law flow can be observed. The melts with higher Mw and/or broader MWD, as well as higher isotacticity exhibit higher complex viscosity, zero shear viscosity, viscoelasticity moduli, relaxation modulus, broader transition zone, while lower critical shear rate, non-Newtonian index, and the frequency at which elasticity begins to play an important role. The relationship of zero shear viscosity on Mw has been established, which agrees with the classical power law. Furthermore, it is found that the cross-over frequency decreases with increasing Mw and the cross-over modulus increases with narrowing MWD.
A series of trans-1,4-butadiene/isoprene copolymers were prepared using the catalyst system TiCl4/MgCl2-Al(iBu)3 with bulk precipitation technology at different temperatures. Monomers reactivity ratios were calculated based on the Kelen-Tüds(K-T) method and the Mao-Huglin(M-H) method. The influence of temperature on copolymer composition and polymerization rate was discussed in detail. The increase of reaction temperature brought the decrease of butadiene reactivity ratio rBd and supplied an effective adjustment on copolymers' composition distribution.