The ultrasonic, magnetic and transport properties of Nd0.5Ca0.5Mn1-xAlxO3 （x=0, 0.03） were studied from 15 to 300 K. The temperature dependencies of resistivity and magnetization show that Nd0.5Ca0.5MnO3 undergoes a charge ordering transition at TCO-257 K. An obvious softening of the longitudinal sound velocity above TCO and a dramatic stiffening below Too accompanied by an attenuation peak were observed. These features imply a strong electron phonom interaction via the Jahn-Teller effect iu the sample, Another broad attenuation peak was observed at around Tp-80 K. This anomaly is attributed to the phase separtion between the antiferromagnetic （AFM） and paramagnetic （PM） phases and gives a direct evidence for spin-phonon coupling in the compound. For the x=0.03 sample, both the minimum of sound velocity and attenuation peaks shift to a lower temperature. The results indicate that the charge ordering and CE-type AFM state in Nd0.5Ca0.5MnO3 are both partially suppressed by replacing Mn with A1.