Yttrium(Y) has been used as the partial substitution element for lanthanum(La) to improve the electrochemical kinetic performances of La-Mg-Ni-based hydrogen storage alloys. La0.80–xYxMg0.20Ni2.85Mn0.10Co0.55Al0.10(x=0.00, 0.05 and 0.10) alloys were prepared by the inductive melting technique. The alloys were composed of La Ni5 and(La,Mg)2Ni7 phases, the introduction of Y promoted the formation of(La,Mg)2Ni7 phase, and thus the Y-substituted alloy electrodes exhibited higher discharge capacities. Y substitution was also found to be effective to improve the discharge kinetics of the alloy electrodes. When the Y content x increased from 0.00 to 0.10, the high-rate dischargeability of the alloy electrodes at a discharge current density of 1800 m A/g(HRD1800) increased from 23.6% to 39.7% at room temperature. In addition, the measured HRD1800 showed a linear dependence on both the exchange current density and the hydrogen diffusion coefficient at different temperatures, respectively.
LaMg8.52Ni2.23M0.15 (M=Ni, Cu, Cr) alloys were prepared by induction melting. X-ray diffraction showed that all the three alloys had a multiphase structure, consisting of La2Mg17, LaMg2Ni and Mg2Ni phases. Energy dispersive X-ray spectrometer results revealed that most of Cu and Cr distributed in Mg2Ni phase. La2Mg17 and LaMg2Ni phases decomposed into MgH2, Mg2NiH4 and LaH3 phases during the hydrogenation process. Hydriding/dehydriding measurements indicated that the reversible hydrogen storage capacities of Mg2Ni phase in LaMg8.52Ni2.23M0.15 (M=Cu, Cr) alloys increased to 1.05 wt.% and 0.97 wt.% from 0.79 wt.% of Mg2Ni phase in LaMg8.52Ni2.38 alloy at 523 K. Partial substitution of Cu and Cr for Ni decreased the onset dehydrogenation temperature of the alloy hydrides and the temperature lowered by 18.20 and 5.50 K, respectively. The improvement in the dehydrogenation property of the alloys was attributed to that Cu and Cr decreased the stability of Mg2NiH4 phase.