Polyaniline(PANI)was effectively immobilized on the surface of ordered mesoporous carbon(OMC)by using Mn_2O_3 as sacrificial template.The observed microstructure and morphology indicate that a thin layer of PANI was coated on OMC uniformly.As a supercapacitor electrode material,the discharge capacity of the optimized PANI/OMC could reach 467 F/g,which is far higher than that of OMC,PANI and Mn_2O_3/OMC.Furthermore,PANI/OMC composites with different content of PANI are obtained by adjusting the amount of Mn_2O_3 on OMC and their properties are characterized.The results show that a thin layer of PANI can improve the capacity of PANI/OMC composites effectively and the further increase of PANI reduces the capacity of PANI/OMC composites.The sacrificial template method presented here is beneficial to coating a layer of polymer on carbon materials,and the content of polymer layer can be controlled by adjusting the amount of Mn_2O_3 in Mn_2O_3/OMC.
Morphology-controlled synthesis and large-scale self-assembly of nanoscale building blocks into complex nanoarchitectures is still a great challenge in nanoscience. In this work, various porous NiO nanostructures are obtained by a simple ammonia precipitation method and we find that the reaction temperature has a significant impact on their microstructures. Nanoflowers and nanoflakes have been obtained at 0 and50, while, weakly self-assembly nanoflowers with nanoflakes are formed at 20. In order to understand the process-structure-property relationship in nanomaterial synthesis and application, the as-prepared NiO is used as supercapacitor electrode materials, and evaluated by electrochemical measurement. The experimental results indicate that the material obtained at lower temperature has higher pseudocapacitance, the specific capacitance of 944, 889 and 410 F/g are reached for the materials prepared at 0, 20 and 50 and further calcined at 300, respectively. While the material obtained at higher temperature has excellent rate capacity. This offers us an opportunity searching for exciting new properties of NiO, and be useful for fabricating functional nanodevices.