Carbon nanotubes (CNTs) reinforced Sn-58Bi composites were successfully fabricated through ball-milling method and low temperature melting process.The influence of multi-walled carbon nanotubes (MWCNTs) on the mechanical strength and ductility of Sn-58Bi lead-free alloy was studied.The mechanical test results show that the bending strength of Sn-58Bi-0.03CNTs (mass fraction,%) composite is increased by 10.5% than that of the Sn-58Bi alloy,which can be attributed to the reduction of Sn-rich segregation and the grain refinement.The toughness of Sn-58Bi-0.03CNTs composite is increased by 48.9% than that of the matrix materials.It is indicated that the influence of CNTs on the strength of Sn-58Bi-xCNTs composite is insignificant.In addition,the fracture mechanism of CNTs reinforced Sn Bi composite was analyzed.The corresponding fracture surface comparison between the Sn-58Bi-0.03CNTs composite and the monolithic Sn-58Bi alloy was made to identify the influence of CNTs on the fracture behavior and the reinforcing effect of CNTs.
Ni-based alloy was transient liquid phase bonded using a BNi-2 interlayer. The effect of bonding parameters on the microstructures and mechanical properties of the joints was investigated. With the increase of bonding temperature or time, the number of Ni-rich and Cr-rich borides and the grain size of precipitation zone decrease. Higher bonding temperature or longer bonding time is beneficial to the diffusion of melting point depressant elements （B and Si） from the PZ to the base metal and atomic interdiffusion between the base metal and the joint. The chemical composition and microstructure of the joints bonded at 1170 ℃ for 24 h are comparable to the base metal. The shear test results show that both the room and elevated temperature shear-strengths of the joints increase with increasing bonding time. However, the effect of bonding time on elevated temperature tensile-shear strength is greater than on room temperature tensile-shear strength.