The influences of W doping at Mn site on the charge order and spin order were studied by measuring M-T curves, M-H curves and ESR spectra of La0.3Ca0.7Mn1?xWxO3 (x = 0.00, 0.04, 0.08, 0.12, 0.15) system. The results showed that: When 0.00≤ x≤0.08, the system exhibits charge ordering (CO) phase, and its spin order experiences the change of paramagnetism (PM)-charge ordering (CO)-antiferro- magnetism (AFM) with decreasing temperature; when x≥0.12, the charge ordering (CO) phase melts, part of charge ordering (CO)phase remains in the paramagnetism (PM)background, the spin order of the system is mainly paramagnetism (PM), and ferromagnetic (FM) clusters appear at low tem- perature.
LIU NingYAN GuoqingCAI ZhirangGUO HuanyinPENG ZhenshengQU ZheZHANG Yuheng
用固相反应法制备了Y1-xDyxCrO3(x=0,0.1)多晶样品。通过X射线衍射(XRD)图谱检测了样品的结构,测量了样品的磁性,作了磁化强度-温度(M-T)曲线、磁化强度-磁场(M-H)曲线,研究了Dy3+替代Y3+对Y1-xDyxCrO3体系磁性质的影响。结果表明,Dy3+替代多铁性YCrO3中的Y3+对YCrO3的磁性有效大影响。YCrO3在奈尔温度TN=139 K以下呈倾角反铁磁,显示弱铁磁性;Dy3+替代Y3+后的Y0.9Dy0.1CrO3样品,在50 K
By measuring M-T curves, ρ-T curves and MR-T curves of the samples under different temperatures, the influence of Dy doping （0.00 ≤ x ≤0.30） on the magnetic and electric properties of La0.7-xDyxSr0.3MnO3 has been studied. The experimental results show that, with the increase of the Dy content, the system undergoes a transition from long range ferromagnetic order to the cluster-spin glass state and further to antiferromagnetic order. For the samples with x=0.20 and 0.30, their magnetic behaviors are abnormal at low temperature, and their resistivities at low temperature have a minimum value. These peculiar phenomena not only come from the lattice effect induced by doping, but also from extra magnetic coupling induced by doping.