A simple and novel method is firstly reported for controlling coffee ring structure on polystyrene（PS）film surface by O2 plasma. O2 plasma treatment leads to the wettability change of PS surface from hydrophobic to hydrophilic. For hydrophilic PS surface the coffee ring structure is avoided relying on the motion of contact line（CL） while SiO2 microspheres are left. The motion of the CL is produced based on the viscosity and Marangoni effect with the addition of polymer additives. For hydrophobic PS surface coffee ring structure still persists even with polymer additives because SiO2 microspheres transfer with the motion of the CL at the beginning of droplet evaporation and accumulate at the droplet edge at late stage with the pinning of the CL. As a result, uniform and macroscale SiO2 microspheres deposition without coffee ring structure and SiO2 microspheres deposition with coffee ring structure are controlled by O2 plasma. This method provides a new way to tune coffee ring structure with smart surface and may be potentially useful for a range of application at material deposition and diagnosing diseases.
Li-Ying CuiYu YanXin-Yu ZhaoCun-Long YuYing MaBai Yang
In the present study,electrostatic atomization(EA)behavior of several test liquids having much higher viscosities(1 400 mPa·s)than have previously been studied was investigated by spraying at a series of applied voltages and flow rates.The results showed that to obtain stable cone-jet mode spraying and hence gain better monodispersity of droplets,electrical conductivity,viscosity and surface tension of the liquid are important controlling factors.The stable cone-jet mode could be easily established for liquids having shear viscosities in the range from 80 to 1 400 mPa·s and surface tensions below 65 mN·m-1.In contrast,methylcellulose aqueous solutions with shear viscosities ranging from 10 to 540 mPa·s and moderate surface tensions(50~56 mN·m-1)generated more complicated spraying modes.However,fine TiO2 powder(a few micrometers in size)could be prepared using the EA method from its precursor solutions.