In this paper,the TiO_2 nanotubes were synthesized by hydrothermal method using a 10 mol/L NaOH aqueous solution at 150℃. The structure of prepared materials was characterized by X-ray diffraction（XRD）,transmission electron microscopy（TEM）. scanning electron microscope（SEM） and Brunauer-Emmett-Teller（BET）.The prepared TiO_2 nanotubes were used to prepare thick film gas sensors and the gas sensing properties to various gases were tested.Results show the prepared TiO_2 nanotube gas sensors responses to ethanol under dry condition at 450℃.This could be attributed to the fact that it had high porous morphology and a higher pore volume,which can promote the diffusion of ethanol deep inside the films and improve the sensor response. Moreover,the gas sensor made with nanotubes exhibit high selective response towards ethanol gas compared with H_2,CO,acetone.
Yan Li Wang Shun Tan Jia Wang Zhi Jin Tan Qiu Xia Wu Zheng Jiao Ming Hong Wu
A facile and general method was described to coat six types of multi-walled carbon nanotubes, functionalized by either noncovalent or covalent way, with smooth silica shells. 3-Aminopropyltriethoxysilane（APTES） and pH value play important roles in the coating process and the thickness of silica shell could be controlled by the added amount of silicon alkoxides. After the removal of multi-walled carbon nanotubes by calcination, the silica nanotubes were successfully prepared.
LI LingDENG Xlao-yongBAI Ming-kunWU Ming-hongLIU Yuan-fang